Efficiency improvement of organic light-emitting diodes depending on the thickness variation of BCP layer used for electron transport

초록

In the devices structure of ITO/N, N'- diph enyl-N, N'bis(3-methylphenyl)- 1, 1'-bipheny1-4, 4'-diam ine(TPD)/tris(8-hydroxyquinoline)aluminum (Alq 3) electron-transport-layer(ETL) (2, 9-Dimethyl-4, 7diphenyl- l, 10-phenanthroline(BCP))/AI, we have studied the efficiency improvement of organic light-emitting diodes depending on the thickness variation of BCP using electron transport layer. The thickness of TPD and Alq3 was manufactured 40nm, 60nm under a base pressure of 5×10-6Torr using at thermal evaporation, respectively. The TPD and Alq, layer were evaporated to be deposition rate of 2.5 Å/s. And the BCP was evaporated to be at a deposition of 1.0Å/s. As the experimental results, we found that the luminous efficiency and the external quantum efficiency of the device is superior to others when thickness of BCP is 5 nm. Also, operating voltage is lowest. Compared to the ones from the devices without BCP layer, the luminous efficiency and the external quantum efficiency were improved by a factor of four hundred ninety and five hundred, respectively. And operating voltage is reduced to about 2 V. ©2009 IEEE.

키워드