Efficient co-host exciplex emission for white organic light-emitting diodes

초록

In this study, white organic light-emitting diodes (WOLEDs) based on exciplexes with a simple structure were investigated. Several combinations of hole-transport material and electron-transport material (ETM) were examined to verify the formation of the exciplexes. Various combinations of these exciplexes contributed to the blue and green emitters, as well as the host within the WOLEDs. Four types of WOLEDs were fabricated using various ETMs 2,2',2 ''-(1,3,5-benzinetriyl)-tris(1-phenyl-1-H-benzimidazole) (TPBi), 4,7-dipheny1-1,10-phenanthroline (BPhen), bis(8-hydroxy-2-methylquinoline)-(4-phenylphenoxy)aluminum (BAIq), and 2,6-bis[3-(9H-carbazol-9-yDphenyl] pyridine (26DCzppy) within the emitting layers (EMLs). In this work, which comprised a blue EML with a 1:1 wt ratio of tris(4-carbazoyl-9-ylphenyl)amine (TCTA) and TPBi, a green EML prepared by mixing 4,4',4 ''-tris[phenyl(m-tolyDamino]triphenylamine (m-MTDATA) and ETMs at a weight ratio of 1:1, and a red EML. In addition, the exciplex formation was optimized according to the mixing concentration of the green EML when BPhen and TPBi were used as the ETM. As a result, a green EML was obtained at 50 wt% TPBi with improved performance, such as an increased power efficiency and a low efficiency roll-off in the range of 200-1000 cd/m(2) in WOLEDs. It also showed white emission for Commission Internationale de l'Eclairage coordinates of (0.45, 0.45) at 1000 cd/m(2).

키워드