High quality PECVD SiO2 process for recessed MOS-gate of AlGaN/GaN-on-Si metal-oxide-semiconductor heterostructure field-effect transistors

초록

A high quality SiO2 deposition process using a plasma enhanced chemical vapor deposition system has been developed for the gate insulator process of normally-off recessed-gate AlGaN/GaN metal-oxide-semiconductor-heterostructure field-effect transistors (MOS-HFETs). SiO2 films were deposited by using SiH4 and N2O mixtures as reactant gases. The breakdown field increased with increasing the N2O flow rate. The optimum SiH4/N2O ratio was 0.05, which resulted in a maximum breakdown field of 11 MV/cm for the SiO2 film deposited on recessed GaN surface. The deposition conditions were optimized as follows; a gas flow rate of SiH4/N2O (=27/540 sccm), a source RF power of 100 W, a pressure of 2 Torr, and a deposition temperature of 350 degrees C. A fabricated normally-off MOS-HFET exhibited a threshold voltage of 3.2 V, a specific on-resistance of 4.46 m Omega cm(2), and a breakdown voltage of 810 V. (C) 2016 Elsevier Ltd. All rights reserved.

키워드