초록

The surface of ZnO nanocrystals was engineered by the creation of an MgO shell layer that prevents the particle aggregation and improves the luminescent properties. The ZnO core with a diameter of similar to 3.0 nm and similar to 0.3 nm thick MgO-passivated ZnO nanocrystals were prepared at 0 degrees C using the reaction between Zn(CH(3)COO)(2), Mg(CH(3)COO)(2) and NaOH dissolved in ethanol medium. While unpassivated or organically capped ZnO nanocrystals are lacking in a colloidal stability against ageing, MgO-passivated ones show a remarkable colloidal stability, demonstrating that the surface passivation of ZnO nanocrystals by an MgO shell is effective. Luminescent efficiencies of green emission of ZnO/MgO nanocrystals versus bare ZnO counterparts are compared, and combined EDS/XPS and Raman spectroscopic data are further provided to verify the core/shell structure of ZnO/MgO nanocrystals.