Temperature- and Frequency-Dependent Ferroelectric Characteristics of Metal-Ferroelectric-Metal Capacitors with Atomic-Layer-Deposited Undoped HfO2 Films

초록

In this study, we evaluated the temperature- and frequency-dependent ferroelectric characteristics of TiN/undoped HfO2/TiN metal-ferroelectric-metal (MFM) capacitors in which an undoped HfO2 film was deposited through atomic layer deposition (ALD). Successful ferroelectric characteristics were achieved after postdeposition annealing at 650 degrees C, which exhibited a remanent polarization of 8 mu C/cm(2) and a coercive electric field of 1.6 MV/cm at 25 degrees C (room temperature). The ferroelectric property was maintained at 200 degrees C and decreased as the temperature increased. The ferroelectric property was completely lost above 320 degrees C and fully recovered after cooling. The frequency dependency was evaluated by bias-dependent capacitance-voltage and s-parameter measurements, which indicated that the ferroelectric property was maintained up to several hundred MHz. This study reveals the ultimate limitations of the application of an undoped HfO2 MFM capacitor.

키워드