Normally-Off GaN-on-Si MISFET Using PECVD SiON Gate Dielectric

초록

We have developed a silicon oxynitride (SiON) deposition process using a plasma-enhanced chemical vapor deposition system for the gate dielectric of GaN-on-Si metal-insulator-semiconductor field-effect transistors (MISFETs). The optimized SiON film had a relative dielectric constant of 5.3 and a breakdown field of 12MV/cm. A normally-off GaN-on-Si MISFET fabricated with a 33-nm SiON gate dielectric exhibited a threshold voltage of similar to 2 V, an ON-resistance of 7.85 m Omega.cm(2), and a breakdown voltage of similar to 640 V at the OFF-state current density of 1 mu A/mm. The extracted interface trap density was 1x10(12) cm(-2) . eV(-1) at E-c - Et = 0.442 eV, which resulted in negligible hysteresis and excellent dynamic characteristics.